PVDF隔膜閥零件材料表
| N0. | 名稱 | 材質 |
| 1 | 螺柱 | 鋼、不銹鋼 |
| 2 | 指示器 | 鋼 |
| 3 | 限位罩 | PC.AS |
| 4 | 墊圈 | 鋼、不銹鋼 |
| 5 | 手輪 | ABS |
| 6 | 壓緊螺母 | 鋼、不銹鋼 |
| 7 | 襯環 | PP |
| 8 | 閥桿螺母 | 鋼、銅HT300 |
| 9 | 閥桿 | 鋼、不銹鋼 |
| 10 | 閥蓋 | PVDF |
| 11 | 平面軸承 | 單向推力球軸承 |
| 12 | 螺母 | 鋼銅、不銹鋼 |
| 13 | 螺柱 | 鋼、不銹鋼 |
| 14 | 閥體 | PVDF |
| 15 | 墊膜 | EPDM.IIR |
| 16 | 膜片 | F46.PFA |
| 17 | 銷 | 鋼、不銹鋼 |
| 18 | 閥瓣 | 鑄鐵、玻璃鋼 |
| 19 | 隔膜 | F46 |
PVDF氣動隔膜閥
| DN | H1 | D1 | D | L | n | c | B |
| 15 | 125 | 65 | 95 | 125 | 4 | 14 | 14 |
| 20 | 130 | 75 | 105 | 135 | 4 | 14 | 16 |
| 25 | 145 | 85 | 115 | 145 | 4 | 14 | 16 |
| 32 | 180 | 100 | 135 | 160 | 4 | 18 | 16 |
| 40 | 220 | 110 | 145 | 180 | 4 | 18 | 16 |
| 50 | 250 | 125 | 160 | 210 | 4 | 18 | 18 |
| 65 | 280 | 145 | 180 | 250 | 4 | 18 | 22 |
| 80 | 340 | 160 | 195 | 300 | 4 | 18 | 25 |
| 100 | 370 | 180 | 215 | 350 | 8 | 18 | 25 |
| 125 | 420 | 210 | 245 | 400 | 8 | 18 | 30 |
| 150 | 480 | 240 | 280 | 460 | 8 | 23 | 30 |
| 200 | 625 | 295 | 335 | 570 | 8 | 23 | 35 |
PVDF性能介紹
PVDF分子結構規整性較大，分子中氟原子和氫原子大小相似，高分子鏈的排列緊密，并存在著較強的氫鍵效應，因此聚合物的拉伸強度，壓縮強度及沖擊韌性等都比較大。PVDF的熔點較低（170℃左右），因此加工性能良好，成型方便，可用一般熱塑料加工方法（如注射、模壓、擠出、吹塑等工藝成型）。它是氟塑料中唯一能制成硬管的材料，廣泛應用在化工管道、泵、閥、墊片、襯里等。
PVDF的化學穩定性良好，具有優良的耐化學腐蝕性和良好的耐熱穩定性，可在此-62℃～150℃溫度范圍內長期使用。同時解電常數大，是良好的絕緣材料之一。不然、耐疲折斷、抗磨損、自潤滑性能好。由于進口燃料，價格昂貴，雖然第一次投入較大，但其價格已經遠遠低于進口管材，并以其優良的耐腐蝕性能，無與倫比的使用壽命、安全系數高、減少維修、將給你帶來顯著的綜合性積極效益。
| 項目 | 數值 | 項目 | 數值 |
| 相對密度 | 1.76 | 拉伸彈性模量（MPa） | 840 |
| 吸水率（%） | 0.04 | 彎曲彈性模量（MPa） | 1400 |
| 晶體熔點（℃） | 171 | 壓縮彈性模量（MPa） | 840 |
| 脆化溫度（℃） | <-61 | 硬度（HB） | 7 |
| 比熱容（J/kg·K） | 1170 | 摩擦系數（對鋼） | 0.14 |
| 線膨脹系數（K） | 80×10 | 介電系數（60Hz） | 8.40 |
| 熱變形溫度：0.46M（℃） | 150 | （106Hz） | 6.43 |
| 1.86MPa | 90 | 介電消耗（60Hz） | 0.05 |
| 分解溫度（℃） | 316 | （106Hz） | 0.16 |
| 工作溫度范圍（℃） | -40～150 | 體積電阻（Ω.cm ） |
2×10 |
| 拉伸強度：25℃（MPa） | 49.2 | 擊穿強度（kv/m ） |
>10 |
| 100（℃） | 35.2 | 耐電弧形（s） | 50-70 |
| 伸長度（%） | 30～400 | 燃燒性 | 自熄 |
| 抗壓強度（MPa） | 70 | 透明性 | 透明-半透明 |
| 沖擊強度（KJ/M2） | 1.47×104 | 耐化學腐蝕性 | 良好 |